High-Temperature Resistant Heat Shrink Tubing FT-VIT200 2:1 Ratio Modified Fluoroelastomer(Viton) tubing
It is especially fit for applications requiring high resistance to corrosive fluids, fuels, lubricants, acids and solvents to prevent wire harnesses , cables and appliances in high temperature environments.
Request a Quote for FT-VIT200 2:1 Ratio Modified Fluoroelastomer(Viton) tubing
- Shrink ratio: 2:1
- Working temperature: -55℃~+200℃
- Shrink temperature: complete shrink at 220℃
- Excellent flame retardant
- Oil resistance and chemical resistance
- Flexibility at high and low temperatures without cracking
- Meets: AMS-DTL-23053/13
Technical Data
| Property | Test Method | Standard |
| Tensile strength(Mpa) | ASTMD 638 | ≥8.5 Mpa |
| Breaking elongation | ASTM D 638 | ≥250 % |
| Operation temperature range | IEC 60216 | -55℃～200℃ |
| Heat aging/Breaking elongation | 168hrs/250℃ | ≥200% |
| Heat shock | 4hrs/330℃ | No cracking |
| Disrup tive strength | ASTM D 2671 | ≥7.9kv/mm |
| Volume resistivity | IEC 60093 | 1X109Ω.cm |
| Size | As Supplied(mm) | After Recovered (mm) | Standard package | ||
| Inch | mm | I.D. Min | I.D. Max. | W.T. Nom. | m/spool |
| 1/8 | 3.2 | 3.2 | 1.6 | 0.76±0.20 | 50 |
| 3/16 | 4.8 | 4.8 | 2.4 | 0.89±0.20 | 50 |
| 1/4 | 6.4 | 6.4 | 3.2 | 0.89±0.20 | 50 |
| 3/8 | 9.5 | 9.5 | 4.8 | 0.89±0.20 | 50 |
| 1/2 | 12.7 | 12.7 | 6.4 | 0.89±0.20 | 50 |
| 3/4 | 19.1 | 19.1 | 9.5 | 1.07±0.30 | 30 |
| 1 | 25.4 | 25.4 | 12.7 | 1.25±0.30 | 30 |
| 1-1/2 | 38.1 | 38.1 | 19.0 | 1.40±0.30 | 15 |
| 2 | 50.8 | 50.8 | 25.4 | 1.65±0.30 | 15 |