High-Temperature Resistant Heat Shrink Tubing FT-PTFE260H 1.7:1 Ratio Modified PTFE (Teflon) tubing
It provides insulation and mechanical protection in severe chemical and high temperature environments to prevent contamination, corrosion and abrasion resistance.
Request a Quote for FT-PTFE260H 1.7:1 Ratio Modified PTFE (Teflon) tubing
- Shrink ratio: 1.7:1
- Working temperature: -65℃~+260℃
- Shrink temperature: complete shrink at 350℃
- Highly flame retardant
- Oil and chemical resistance
- Excellent insulation, abrasion resistance
- Meet SAE-AMS-DTL-23053/12
Technical Data
| Property | Test Method | Standard |
| Tensile strength | ASTM D 2671 | ≥ 17.3 MPa |
| Breaking elongation | ASTM D 2671 | ≥ 200 % |
| Specific gravity | ASTM D 792 | 2.3g/cm3 |
| Heat shock | 4hrs 400℃ | No cracking or dropping |
| Cold bend | 4hrs -65℃ | No cracking |
| Dielectric strength | ASTM D 2671 | ≥ 34kV/mm |
| Volume resistivity | ASTM D 2671 | 1X1018 Ω.cm |
| Size | As Supplied(mm) | After Recovered (mm) | Standard Packing | ||
| AWG | mm | I.D. Min | I.D. Max. | W.T. Nom. | m/spool |
| 26 | 1.1 | 1.1±0.20 | ≤ 0.60 | 0.25±0.05 | 200 |
| 20 | 1.5 | 1.5±0.20 | ≤ 1.00 | 0.30±0.08 | 200 |
| 18 | 2.0 | 2.0±0.20 | ≤ 1.25 | 0.30±0.08 | 200 |
| 16 | 2.3 | 2.3±0.20 | ≤ 1.60 | 0.30±0.08 | 100 |
| 14 | 3.0 | 3.0±0.20 | ≤ 1.85 | 0.30±0.08 | 100 |
| 12 | 3.8 | 3.8±0.20 | ≤ 2.3 | 0.30±0.08 | 100 |
| 10 | 4.8 | 4.8±0.30 | ≤ 2.85 | 0.30±0.08 | 100 |
| 8 | 6.1 | 6.1±0.30 | ≤ 3.6 | 0.38±0.08 | 1.22m/pcs |
| 6 | 7.6 | 7.6±0.30 | ≤ 4.5 | 0.38±0.08 | 1.22m/pcs |
| 4 | 9.4 | 9.4±0.30 | ≤ 5.7 | 0.38±0.08 | 1.22m/pcs |
| 2 | 10.9 | 10.9±0.30 | ≤ 7.1 | 0.38±0.08 | 1.22m/pcs |
| 0 | 11.9 | 12.0±0.30 | ≤ 8.8 | 0.38±0.08 | 1.22m/pcs |